Abstract
The effects of high-basicity pellet on smelting chromium-bearing vanadia-titania magnetite are investigated via thermodynamic smelting and non-isothermal kinetics experiments. The thermodynamic results indicated that the high-basicity pellet significantly affects and ameliorates the softening-melting-dripping behaviors during the smelting process. As the high-basicity pellet ratio increased from 0 wt.% to 52 wt.%, the range of softening temperature [T40−T4] decreased from 121 °C to 84 °C and the melting-dripping temperature [Td−Ts] decreased from 224 °C to 169 °C. Moreover, the apparent activation energy of non-isothermal kinetics also decreased from 99.91 kJ·mol−1 to 66.74 kJ·mol−1. Additionally, the reaction mechanism of high-basicity pellet on smelting chromium-bearing vanadia-titania magnetite was investigated via thermodynamic calculations of Gibbs free energy and characterizations of the titanium slag. Therefore, combined with the lowest permeability index, the fastest non-isothermal reduction rate, the highest recovery of valuable elements and the minimum content of titanium carbonitride, the preferable high-basicity pellet ratio was considered to be 11~23 wt.%.