Abstract
The influence of hydrothermal pretreatment temperature on the hydration products and carbonation efficiency of Al-rich LF slag was investigated. The results showed that the carbonation efficiency was strongly dependent on the morphology of hydration products and the hydration extent of the raw slag. Hydrothermal pretreatment at 20 °C or 80 °C favored the formation of flake-shaped products with a higher specific surface area and therefore resulted in a higher CO2 uptake of 20 °C and 80 °C-pretreated slags (13.66 wt% and 10.82 wt%, respectively). However, hydrothermal pretreatment at 40 °C, 60 °C or 100 °C led to the rhombohedral-shaped calcite layer surrounding the unreacted core of the raw slag and the formation of fewer flake-shaped products, resulting in a lower CO2 uptake of 40 °C, 60 °C and 100 °C-pretreated slags (9.21 wt%, 9.83 wt%, and 6.84 wt%, respectively).