Abstract
Nuclear graphite can be used in fission and fusion systems due to its excellent nuclear performance and mechanical properties where the ability of oxidation resistance is usually concerned. Although the excellent performance of new graphite ET-10 was revealed by previous experiments regarding the accident conditions of a fission reactor, further studies are needed to oxidize the graphite under the conditions recommended by the ASTM D7542 standard. A test facility was designed and developed to oxidize the cylindrical specimen with a 10 L/min airflow. According to oxidation rates and microstructures of specimens, the chemical kinetics-controlled regime was determined as 675−750 °C, where the activation energy was obtained as 172.52 kJ/mol. The experiment results revealed the excellent ability of graphite ET-10 for oxidation resistance with lower oxidation rates and longer oxidation times compared with some mainstream graphite. The main reasons are the low contents of some impurities and the binder and the low active surface area due to the non-impregnation baking process undertaken to produce graphite with coal tar pitch coke. It should be noted that the evolution of oxidation behavior at the bottom part of the specimen (facing the airflow) was quicker than that at the upper part of the specimen. We also suggest that the abundance of oxygen supply and the good linearity of the Arrhenius plot are prerequisites of the chemical kinetics-controlled regime rather than sufficient conditions.