Abstract
Sodium sulfate (SS) is a neutral activator. SS-activated alkali-activated slag cement (AASC) has lower shrinkage. However, it sets slowly, and the mechanical property develops slowly. Slaked lime (SL) is an alkaline substance widely used in industry that can be used as an activator in AASC. In this paper, SL was used alone, and SL and SS were mixed together to prepare AASC. The effects of SL content on the setting time, shrinkage properties and mechanical strength of AASC were investigated. Furthermore, the mechanism was explored with the analysis of microscopic tests. The results showed that SS could not be used as an activator alone, while SL could be used as an activator alone, and SS could be combined with SL to prepare AASC. The setting time of the SL system or the SS-SL mix system decreased with the increase in SL. The mechanical properties of the SL system were poor. The SS-SL system showed the highest mechanical properties when SL was 3%. With the increase in SL, the autogenous and drying shrinkage of the SL system increased, while the former of the SS-SL system increased and the latter decreased. At the same time, due to the different changes in pore structure and mesoporous volume in the two systems, the drying shrinkage showed different changes. Compared with the SL system, ettringite (AFt) with a slight expansion property and more crystal phases were formed in the SS-SL system, which reduced the drying shrinkage.