Abstract
The potential of the supercritical antisolvent micronization (SAS) technique was evaluated for the production of CaO-based particles with a size and a physical structure that could enable high performance for CO2 capture through the calcium looping process. Two sources of calcium derivative compounds were tested, waste marble powder (WMP) and dolomite. The SAS micronization of the derivate calcium acetate was carried out at 60 °C, 200 bar, a 0.5 mL min−1 flow rate of liquid solution, and 20 mg mL−1 concentration of solute, producing, with a yield of more than 70%, needle-like particles. Moreover, since dolomite presents with a mixture of calcium and magnesium carbonates, the influence of the magnesium fraction in the SAS micronization was also assessed. The micronized mixtures with lower magnesium content (higher calcium fraction) presented needle-like particles similar to WMP. On the other hand, for the higher magnesium fractions, the micronized material was similar to magnesium acetate micronization, presenting sphere-like particles. The use of the micronized material in the Ca-looping processes, considering 10 carbonation-calcination cycles under mild and realistic conditions, showed that under mild conditions, the micronized WMP improved CaO conversion. After 10 cycles the micronization, WMP presented a conversion 1.8 times greater than the unprocessed material. The micronized dolomite, under both mild and real conditions, maintained more stable conversion after 10 cycles.